MKW 136

MKW 136 is a thick-bed, , cement based marble and granite adhesive. It is polymer modified and suitable for applications on horizontal and vertical surfaces. It consists of cement, mineral fillers and admixtures. It is classified as type C2T according to EN 12004.

• Suitable for fixing marble and granite on mineral and vertical substrates in dry and wet duty rooms

• It prevents staining of marble elements and is qualified as a slip resistant tile adhesive which means that tile does not slip at all on vertical surfaces
• It has high resistance to weather conditions (storm, heat and freezing)
• It exhibits thixotropic properties

• The tile-layering sub-layer must be flat, free from brittle and foreign bodies such as for example plaster residue, paint, oils, etc. It must be stable free from. istortions and must not be subject to vibrations. The absorbent sub-layers are primed using GLX 290 primer before application.
• In a clean container add 4.5-5.0 liters of clean water and gradually empty the content of a 25 Kg sack of product FSW 140, mixing continuously with an electric mixer in order to acquire a uniform grout mass. Let the resulting mixture age for 5 minutes and mix again.
• The mixture is ready to be used within the next 1.5 hours.
• ain. The mixture is ready to be used within the next 1.5 hours. Following the preparation of the mixture do not add more water in order to correct the workability of the slurry. This would lead to the reduction of its tolerances and the increase of its shrinkage.
• This would lead to the reduction of its tolerances and the increase of its shrinkage The open time for application is 10min.
• Following completion of the application clean the surface with a wet sponge.
• The open time for application is 10min. Any excess adhesive must be removed from the joints.
• After the lapse of 1-2 hours from the application of the grout on the firebricks, perform mounting using the same product.
• Prior to the initial usage of the fireplace, oven, etc, the grout must be fully dried. It is recommended that the initial operation is performed after 10 days.
• During application and for the next 24 hours the environmental and sub-layer temperature must be between +5_oC and +35_oC.
• The adhesive is cleaned with water while still wet. When it hardens it is removed mechanically.

In a dry environment at temperatures above 0_oC for 12 months its production date.